1 1

61newmaterial

Industrial Thermal Insulation (and Cold Insulation) Coatings

Industrial Thermal Insulation (and Cold Insulation) Coatings

$0.00 USD
$0.00 USD
Sale Sold out

Product Introduction:
Compared with traditional thermal (and cold) insulation materials, our aerogel coatings offer significant advantages in construction convenience and comprehensive cost-performance. They not only enable easy installation but also address the key drawbacks of common organic insulators (e.g., polyurethane, rubber-plastic sponge), such as poor fire resistance, low flame retardancy, and high construction difficulty—especially for renovation projects on existing equipment pipelines.

1. Product Overview 

Item Detail
Product Name Industrial Thermal Insulation (and Cold Insulation) Coatings
Model LYAC-C-I
Functions Cold insulation, energy saving, condensation prevention
Temperature Range -40~100℃
Packaging Sizes 5L / 19L / 30L
Gloss Matte, color adjustable
Theoretical Paint Consumption Calculated based on energy-saving indicators
Coating Layers Dependent on working conditions
Coating Area 1m²/L/single coat (based on 1mm dry film thickness)
Storage Instructions Keep sealed, store at 5~35℃

2. Technical Parameters

Item Parameter Test Standard
Color White (color 可调) -
Thermal Conductivity 0.025~0.03 W/(m·K) GB/T 10295-2008 (Heat Flow Method)
Density 0.50~0.55 g/cm³ GB/T 1033-1986
Viscosity (KU) >135 GB/T 1723-1993
Water Resistance 96h, no abnormality DBJ43/T 371-2021
Alkali Resistance 48h, no abnormality GB/T 8756-2018
VOC Content <2g/L (未检出) GB 18582-2020
Weather Aging Test Excellent after 2000h GB/T 1765-1989
Adhesion >0.8 mPa GB/T 5210-2006

3. Application Recommendations

Substrate Type Layer Structure Notes
Stainless steel, aluminum Substrate + cold insulation coating + wear-resistant waterproof topcoat Wear-resistant topcoat is optional.
Carbon steel, copper Substrate + anti-rust primer + cold insulation coating + wear-resistant waterproof topcoat -
Rusty iron substrate Substrate + rust conversion primer + anti-rust primer + cold insulation coating + wear-resistant waterproof topcoat -

4.

Process Method Instructions
Brush coating Single-direction brushing, single-layer thickness <2mm Simple tools, easy to use, low material loss, low odor; poor smoothness, low efficiency.
Trowel coating Trowel with screed for leveling, single-layer thickness <2mm Simple tools, easy to use, low material loss, low odor; difficult for irregular parts.
Air compressor spraying (non-atomized) Air pressure: 0.6-0.8MPa
Nozzle diameter: 6-8mm
Single-layer thickness ≤2mm		 Suitable for true stone paint/putty spraying equipment, high efficiency; creates a textured surface.
Air compressor spraying (atomized) Adjust viscosity <130KU with water before use
Air pressure: 0.6-0.8MPa
Nozzle diameter: 2.5-3mm
Single-layer thickness ≤1mm		 Good atomization, smooth film surface; high material loss, requires strict protection.

 

Compared with traditional thermal (and cold) insulation materials, it has advantages in product construction and comprehensive cost-performance ratio. Aerogel coatings not only offer convenient construction but also make up for the defects of common organic thermal insulation materials (such as polyurethane and rubber-plastic sponge), such as poor fire resistance and flame retardancy, high construction difficulty, especially for the construction and renovation of existing equipment pipelines.
View full details